Table 1 Summary of Test Data for HSS and VHSS at elevated temperatures
From: Mechanical properties of High and Very High Steel at elevated temperatures and after cooling down
Source | Number of specimens | Number of curves | Manufacture process | Steel type | Average f y (MPa) | T (°C) |
|---|---|---|---|---|---|---|
Holt (Unknown) | 10 | - | quenched and tempered | ASTM A514 | 816 | 27–1038 |
USS (1972) | 10 | - | quenched and tempered | ASTM A514 | 803 | 27–1038 |
NIST TN1714 | 10 | - | quenched and tempered | - | 760 | 20–701 |
Chen et al. (2006) | 34 | 12 | quenched and tempered | S690Q | 789 | 60–940 |
Qiang et al. (2013a) | 26 | 12 | normalized | S460 N | 510 | 100–700 |
Choi et al. (2014) | 10 | 10 | quenched and tempered | HSA 800 | 701 | 100–900 |
Wang et al. (2013) | 22 | 11 | alloy steel | Q460 | 503 | 100–800 |
Heidarpour et al. (2014) | 14 | 14 | quenched and tempered | VHS | 1307 | 50–600 |
Chiew et al. (2014) | 10 | 10 | reheated, quenched and tempered | RQT-S690 | 773 | 100–800 |
Xiong and Liew (2016) | 18 | 17 | quenched and tempered | RQT 701 | 740 | 100–800 |
Lazić et al. (2016) | 22 | 10 | quenched and tempered | S690QL | 775 | 250–550 |
Qiang et al. (2016) | 24 | 24 | quenched and tempered | S960QL | 1045 | 100–700 |